"Modification" "CrystalSystem" "Temperature" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "SpaceGroup" "Comment" "&alpha;" "Monoclinic" "0" "3.2" "0" "37" "" "" "&alpha;" "Monoclinic" "77" "2.8" "0" "34" "" "" "&alpha;" "Monoclinic" "77" "3.1" "0" "34" "" "" "&alpha;" "Monoclinic" "300" "2.6" "0" "34" "" "" "&alpha;" "Monoclinic" "300" "2.85" "0" "34" "" "" "&alpha;" "Monoclinic" "77" "3.1" "0" "581" "P2<sub>1</sub>/c" "" "&alpha;" "Monoclinic" "300" "2.15" "0" "581" "P2<sub>1</sub>/c" "Thermal activation. Direct transition. Thin film, polycristalline" "&alpha;" "Monoclinic" "300" "2.58" "0" "581" "P2<sub>1</sub>/c" "Photoconduction. Thin film, polycristalline" "&alpha;" "Monoclinic" "300" "2.6" "0" "581" "P2<sub>1</sub>/c" "Optical absorption spectroscopy. Indirect transition. Thin film, polycristalline" "&alpha;" "Monoclinic" "300" "2.85" "0" "581" "P2<sub>1</sub>/c" "Optical absorption spectroscopy. Thin film, polycristalline" "&alpha;" "Monoclinic" "300" "2.85" "0" "581" "P2<sub>1</sub>/c" "Photoconduction. Thin film, polycristalline" "&alpha;" "Monoclinic" "300" "2.86" "0" "581" "P2<sub>1</sub>/c" "Diffuse reflectance spectroscopy. Polycristalline" "&alpha;" "Monoclinic" "300" "2.91" "0" "581" "P2<sub>1</sub>/c" "Optical absorption spectroscopy. Thin film, polycristalline" "&alpha;" "Monoclinic" "400" "2.07" "0" "581" "P2<sub>1</sub>/c" "Thermal activation. Thin film, polycristalline" "&epsilon;" "Orthorhombic" "" "2.6" "0" "1398" "" "Optical"

Chart

X axis: Y axis:

CSV Viewer: BI2O3

Modification CrystalSystem Temperature Eg IsCalculated ReferenceId SpaceGroup Comment
α Monoclinic 0 3.2 0 37
α Monoclinic 77 2.8 0 34
α Monoclinic 77 3.1 0 34
α Monoclinic 300 2.6 0 34
α Monoclinic 300 2.85 0 34
α Monoclinic 77 3.1 0 581 P21/c
α Monoclinic 300 2.15 0 581 P21/c Thermal activation. Direct transition. Thin film, polycristalline
α Monoclinic 300 2.58 0 581 P21/c Photoconduction. Thin film, polycristalline
α Monoclinic 300 2.6 0 581 P21/c Optical absorption spectroscopy. Indirect transition. Thin film, polycristalline
α Monoclinic 300 2.85 0 581 P21/c Optical absorption spectroscopy. Thin film, polycristalline
α Monoclinic 300 2.85 0 581 P21/c Photoconduction. Thin film, polycristalline
α Monoclinic 300 2.86 0 581 P21/c Diffuse reflectance spectroscopy. Polycristalline
α Monoclinic 300 2.91 0 581 P21/c Optical absorption spectroscopy. Thin film, polycristalline
α Monoclinic 400 2.07 0 581 P21/c Thermal activation. Thin film, polycristalline
ε Orthorhombic 2.6 0 1398 Optical