"CrystalSystem" "SpaceGroup" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "Temperature" "StructureType" "Comment"
"Cubic" "Pn3m" "2.08" "0" "29" "" "" ""
"Cubic" "Pn3m" "2.08" "0" "37" "" "" ""
"Cubic" "Pn3m" "2" "0" "37" "0" "" ""
"Cubic" "Pn3m" "2.17" "0" "30" "4.2" "" ""
"Cubic" "Pn3m" "2.17" "0" "33" "4.2" "" ""
"Cubic" "Pn3m" "1.5" "0" "27" "300" "" ""
"Cubic" "Pn3m" "1.56" "0" "37" "300" "" ""
"Cubic" "Pn3m" "1.9" "0" "37" "300" "" ""
"Cubic" "Pn3m" "2.1" "0" "37" "300" "" ""
"Cubic" "Pn3(-)m" "2.17" "0" "581" "0" "Cu<sub>2</sub>O" "Diffuse reflectance spectroscopy. Excitonic transition. Thin film, polycristalline"
"Cubic" "Pn3(-)m" "2.58" "0" "581" "0" "Cu<sub>2</sub>O" "Diffuse reflectance spectroscopy. Thin film, polycristalline"
"Cubic" "Pn3(-)m" "2.023" "0" "581" "77" "Cu<sub>2</sub>O" "Electroreflection. Indirect transition. Polycristalline"
"Cubic" "Pn3(-)m" "2.59" "0" "581" "293" "Cu<sub>2</sub>O" "Electroreflection"
"Cubic" "Pn3(-)m" "2.02" "0" "581" "300" "Cu<sub>2</sub>O" "Diffuse reflectance spectroscopy. Polycristalline"
"Cubic" "Pn3(-)m" "2.67" "0" "581" "300" "Cu<sub>2</sub>O" "Diffuse reflectance spectroscopy. Polycristalline"
Chart
X axis:
Y axis:
CSV Viewer: Cu2O
| CrystalSystem | SpaceGroup | Eg | IsCalculated | ReferenceId | Temperature | StructureType | Comment |
|---|---|---|---|---|---|---|---|
| Cubic | Pn3m | 2.08 | 0 | 29 | |||
| Cubic | Pn3m | 2.08 | 0 | 37 | |||
| Cubic | Pn3m | 2 | 0 | 37 | 0 | ||
| Cubic | Pn3m | 2.17 | 0 | 30 | 4.2 | ||
| Cubic | Pn3m | 2.17 | 0 | 33 | 4.2 | ||
| Cubic | Pn3m | 1.5 | 0 | 27 | 300 | ||
| Cubic | Pn3m | 1.56 | 0 | 37 | 300 | ||
| Cubic | Pn3m | 1.9 | 0 | 37 | 300 | ||
| Cubic | Pn3m | 2.1 | 0 | 37 | 300 | ||
| Cubic | Pn3(-)m | 2.17 | 0 | 581 | 0 | Cu2O | Diffuse reflectance spectroscopy. Excitonic transition. Thin film, polycristalline |
| Cubic | Pn3(-)m | 2.58 | 0 | 581 | 0 | Cu2O | Diffuse reflectance spectroscopy. Thin film, polycristalline |
| Cubic | Pn3(-)m | 2.023 | 0 | 581 | 77 | Cu2O | Electroreflection. Indirect transition. Polycristalline |
| Cubic | Pn3(-)m | 2.59 | 0 | 581 | 293 | Cu2O | Electroreflection |
| Cubic | Pn3(-)m | 2.02 | 0 | 581 | 300 | Cu2O | Diffuse reflectance spectroscopy. Polycristalline |
| Cubic | Pn3(-)m | 2.67 | 0 | 581 | 300 | Cu2O | Diffuse reflectance spectroscopy. Polycristalline |