"CrystalSystem" "StructureType" "SpaceGroup" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "Comment" "Temperature" "Cubic" "ZnS" "F4(-)3m" "1.42" "0" "31" "" "" "Cubic" "ZnS" "F4(-)3m" "1.424" "0" "31" "" "" "Cubic" "ZnS" "F4(-)3m" "1.426" "0" "27" "" "" "Cubic" "ZnS" "F4(-)3m" "1.43" "0" "30" "" "" "Cubic" "ZnS" "F4(-)3m" "1.43" "0" "36" "" "" "Cubic" "ZnS" "F4(-)3m" "1.5115" "0" "31" "" "" "Cubic" "ZnS" "F4(-)3m" "1.53" "0" "27" "" "" "Cubic" "ZnS" "F4(-)3m" "1.53" "0" "36" "" "" "Cubic" "ZnS" "F4(-)3m" "1.53" "0" "37" "" "" "Cubic" "ZnS" "F4(-)3m" "1.53" "0" "27" "Film" "" "Cubic" "ZnS" "F4(-)3m" "1.58" "0" "50" "" "" "Cubic" "ZnS" "F4(-)3m" "1.75" "0" "152" "5 GPa" "" "Cubic" "ZnS" "F4(-)3m" "1.4" "0" "36" "" "0" "Cubic" "ZnS" "F4(-)3m" "1.522" "0" "27" "" "0" "Cubic" "ZnS" "F4(-)3m" "1.58" "0" "37" "" "0" "Cubic" "ZnS" "F4(-)3m" "1.5192" "0" "31" "" "2" "Cubic" "ZnS" "F4(-)3m" "1.52" "0" "30" "" "2" "Cubic" "ZnS" "F4(-)3m" "1.52" "0" "35" "" "2" "Cubic" "ZnS" "F4(-)3m" "1.52" "0" "37" "" "2" "Cubic" "ZnS" "F4(-)3m" "1.517" "0" "36" "" "4" "Cubic" "ZnS" "F4(-)3m" "1.5177" "0" "31" "" "4.2" "Cubic" "ZnS" "F4(-)3m" "1.521" "0" "31" "" "20" "Cubic" "ZnS" "F4(-)3m" "1.5114" "0" "31" "" "77" "Cubic" "ZnS" "F4(-)3m" "1.511" "0" "31" "" "90" "Cubic" "ZnS" "F4(-)3m" "1.435" "0" "31" "" "240" "Cubic" "ZnS" "F4(-)3m" "1.4257" "0" "31" "" "297" "Cubic" "ZnS" "F4(-)3m" "1.42" "0" "72" "Direct transition" "298" "Cubic" "ZnS" "F4(-)3m" "1.425" "0" "72" "Direct transition" "298" "Cubic" "ZnS" "F4(-)3m" "1.428" "0" "72" "Direct transition" "298" "Cubic" "ZnS" "F4(-)3m" "1.43" "0" "72" "Direct transition" "298" "Cubic" "ZnS" "F4(-)3m" "1.435" "0" "72" "Direct transition" "298" "Cubic" "ZnS" "F4(-)3m" "1.428" "0" "27" "" "300" "Cubic" "ZnS" "F4(-)3m" "1.35" "0" "31" "" "473" "Cubic" "ZnS" "F4(-)3m" "1.147" "0" "31" "" "873" "Cubic" "ZnS" "F4(-)3m" "1.09" "0" "31" "" "973" "Tetragonal" "" "" "1.35" "0" "37" "" ""

Chart

X axis: Y axis:

CSV Viewer: GaAs

CrystalSystem StructureType SpaceGroup Eg IsCalculated ReferenceId Comment Temperature
Cubic ZnS F4(-)3m 1.42 0 31
Cubic ZnS F4(-)3m 1.424 0 31
Cubic ZnS F4(-)3m 1.426 0 27
Cubic ZnS F4(-)3m 1.43 0 30
Cubic ZnS F4(-)3m 1.43 0 36
Cubic ZnS F4(-)3m 1.5115 0 31
Cubic ZnS F4(-)3m 1.53 0 27
Cubic ZnS F4(-)3m 1.53 0 36
Cubic ZnS F4(-)3m 1.53 0 37
Cubic ZnS F4(-)3m 1.53 0 27 Film
Cubic ZnS F4(-)3m 1.58 0 50
Cubic ZnS F4(-)3m 1.75 0 152 5 GPa
Cubic ZnS F4(-)3m 1.4 0 36 0
Cubic ZnS F4(-)3m 1.522 0 27 0
Cubic ZnS F4(-)3m 1.58 0 37 0
Cubic ZnS F4(-)3m 1.5192 0 31 2
Cubic ZnS F4(-)3m 1.52 0 30 2
Cubic ZnS F4(-)3m 1.52 0 35 2
Cubic ZnS F4(-)3m 1.52 0 37 2
Cubic ZnS F4(-)3m 1.517 0 36 4
Cubic ZnS F4(-)3m 1.5177 0 31 4.2
Cubic ZnS F4(-)3m 1.521 0 31 20
Cubic ZnS F4(-)3m 1.5114 0 31 77
Cubic ZnS F4(-)3m 1.511 0 31 90
Cubic ZnS F4(-)3m 1.435 0 31 240
Cubic ZnS F4(-)3m 1.4257 0 31 297
Cubic ZnS F4(-)3m 1.42 0 72 Direct transition 298
Cubic ZnS F4(-)3m 1.425 0 72 Direct transition 298
Cubic ZnS F4(-)3m 1.428 0 72 Direct transition 298
Cubic ZnS F4(-)3m 1.43 0 72 Direct transition 298
Cubic ZnS F4(-)3m 1.435 0 72 Direct transition 298
Cubic ZnS F4(-)3m 1.428 0 27 300
Cubic ZnS F4(-)3m 1.35 0 31 473
Cubic ZnS F4(-)3m 1.147 0 31 873
Cubic ZnS F4(-)3m 1.09 0 31 973
Tetragonal 1.35 0 37