Materials Library Visualization
"Modification" "CrystalSystem" "StructureType" "SpaceGroup" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "Comment" "Temperature"
"KI" "Hexagonal" "BN" "P6<sub>3</sub>/mmc" "3" "0" "43" "" ""
"KI" "Hexagonal" "BN" "P6<sub>3</sub>/mmc" "5.9" "0" "31" "" ""
"KI" "Hexagonal" "BN" "P6<sub>3</sub>/mmc" "3.8" "0" "27" "at 200 K" ""
"KI" "Hexagonal" "BN" "P6<sub>3</sub>/mmc" "3.85" "0" "27" "" ""
"KI" "Hexagonal" "BN" "P6<sub>3</sub>/mmc" "4.5" "0" "31" "" ""
"KI" "Hexagonal" "BN" "P6<sub>3</sub>/mmc" "4.5" "0" "27" "ΔE > 4.5 eV" ""
"KI" "Hexagonal" "BN" "P6<sub>3</sub>/mmc" "5.8" "0" "31" "" ""
"KI" "Hexagonal" "BN" "P6<sub>3</sub>/mmc" "6.2" "0" "31" "" ""
"KI" "Hexagonal" "BN" "P6<sub>3</sub>/mmc" "10" "0" "37" "" ""
"KI" "Hexagonal" "BN" "P6<sub>3</sub>/mmc" "3.6" "0" "27" "KI -->KII" "300"
"KII" "Cubic" "sphalerite" "F4(-)3m" "8" "1" "581" "Indirect transition. Calculation (APW method)" "300"
"KII" "Cubic" "ZnS" "F4(-)3m" "4.6" "0" "37" "" ""
"KII" "Cubic" "ZnS" "F4(-)3m" "4.6" "0" "43" "" ""
"KII" "Cubic" "ZnS" "F4(-)3m" "5" "0" "37" "" ""
"KII" "Cubic" "ZnS" "F4(-)3m" "6.4" "0" "31" "" ""
"KII" "Cubic" "ZnS" "F4(-)3m" "6.4" "0" "27" "at 300 K; ΔE > 6.4 eV" ""
"KII" "Cubic" "ZnS" "F4(-)3m" "8" "0" "31" "" ""
"KII" "Cubic" "ZnS" "F4(-)3m" "14.5" "0" "31" "" ""
"KII" "Cubic" "ZnS" "F4(-)3m" "6" "0" "27" "KII -->KIII; ΔE < 6 eV" "300"
"KII" "Cubic" "ZnS" "F4(-)3m" "6" "0" "31" "KII -->KIII; ΔE < 6 eV" "300"
"KIII" "Hexagonal" "ZnS" "P6<sub>3</sub>mc" "3.4" "0" "27" "Film" "300"
Chart
X axis:
Y axis:
CSV Viewer: BN
| Modification | CrystalSystem | StructureType | SpaceGroup | Eg | IsCalculated | ReferenceId | Comment | Temperature |
|---|---|---|---|---|---|---|---|---|
| KI | Hexagonal | BN | P63/mmc | 3 | 0 | 43 | ||
| KI | Hexagonal | BN | P63/mmc | 5.9 | 0 | 31 | ||
| KI | Hexagonal | BN | P63/mmc | 3.8 | 0 | 27 | at 200 K | |
| KI | Hexagonal | BN | P63/mmc | 3.85 | 0 | 27 | ||
| KI | Hexagonal | BN | P63/mmc | 4.5 | 0 | 31 | ||
| KI | Hexagonal | BN | P63/mmc | 4.5 | 0 | 27 | ΔE > 4.5 eV | |
| KI | Hexagonal | BN | P63/mmc | 5.8 | 0 | 31 | ||
| KI | Hexagonal | BN | P63/mmc | 6.2 | 0 | 31 | ||
| KI | Hexagonal | BN | P63/mmc | 10 | 0 | 37 | ||
| KI | Hexagonal | BN | P63/mmc | 3.6 | 0 | 27 | KI -->KII | 300 |
| KII | Cubic | sphalerite | F4(-)3m | 8 | 1 | 581 | Indirect transition. Calculation (APW method) | 300 |
| KII | Cubic | ZnS | F4(-)3m | 4.6 | 0 | 37 | ||
| KII | Cubic | ZnS | F4(-)3m | 4.6 | 0 | 43 | ||
| KII | Cubic | ZnS | F4(-)3m | 5 | 0 | 37 | ||
| KII | Cubic | ZnS | F4(-)3m | 6.4 | 0 | 31 | ||
| KII | Cubic | ZnS | F4(-)3m | 6.4 | 0 | 27 | at 300 K; ΔE > 6.4 eV | |
| KII | Cubic | ZnS | F4(-)3m | 8 | 0 | 31 | ||
| KII | Cubic | ZnS | F4(-)3m | 14.5 | 0 | 31 | ||
| KII | Cubic | ZnS | F4(-)3m | 6 | 0 | 27 | KII -->KIII; ΔE < 6 eV | 300 |
| KII | Cubic | ZnS | F4(-)3m | 6 | 0 | 31 | KII -->KIII; ΔE < 6 eV | 300 |
| KIII | Hexagonal | ZnS | P63mc | 3.4 | 0 | 27 | Film | 300 |