Materials Library Visualization

"CrystalSystem" "Temperature" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "StructureType" "SpaceGroup" "Comment" "Cubic" "4.2" "3.201" "0" "32" "" "" "" "Cubic" "4.2" "3.2052" "0" "32" "" "" "" "Cubic" "4.2" "3.2682" "0" "32" "" "" "" "Cubic" "4.2" "3.2754" "0" "32" "" "" "" "Cubic" "4.2" "3.395" "0" "32" "" "" "" "Cubic" "8" "3.202" "0" "32" "" "" "" "Cubic" "8" "3.203" "0" "32" "" "" "" "Cubic" "8" "3.273" "0" "32" "" "" "" "Cubic" "8" "3.275" "0" "32" "" "" "" "Cubic" "80" "3.221" "0" "32" "" "" "" "Cubic" "80" "3.222" "0" "32" "" "" "" "Cubic" "80" "3.237" "0" "32" "" "" "" "Cubic" "80" "3.294" "0" "32" "" "" "" "Cubic" "80" "3.306" "0" "32" "" "" "" "Cubic" "300" "3.395" "0" "32" "" "" "" "Cubic" "80" "3.306" "0" "581" "sphalerite" "F4(-)3m" "Optical absorption spectroscopy. Excitonic transition. Thin film, polycristalline"

Chart

X axis: Y axis:

CSV Viewer: CuCl

CrystalSystem Temperature Eg IsCalculated ReferenceId StructureType SpaceGroup Comment
Cubic 4.2 3.201 0 32
Cubic 4.2 3.2052 0 32
Cubic 4.2 3.2682 0 32
Cubic 4.2 3.2754 0 32
Cubic 4.2 3.395 0 32
Cubic 8 3.202 0 32
Cubic 8 3.203 0 32
Cubic 8 3.273 0 32
Cubic 8 3.275 0 32
Cubic 80 3.221 0 32
Cubic 80 3.222 0 32
Cubic 80 3.237 0 32
Cubic 80 3.294 0 32
Cubic 80 3.306 0 32
Cubic 300 3.395 0 32
Cubic 80 3.306 0 581 sphalerite F4(-)3m Optical absorption spectroscopy. Excitonic transition. Thin film, polycristalline