"Modification" "CrystalSystem" "StructureType" "SpaceGroup" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "Temperature" "Comment"
"α" "Hexagonal" "Na<sub>3</sub>As" "P6<sub>3</sub>/mmc" "1.3" "0" "33" "" ""
"α" "Hexagonal" "Na<sub>3</sub>As" "P6<sub>3</sub>/mmc" "1.1" "0" "37" "0" ""
"α" "Hexagonal" "Na<sub>3</sub>As" "P6<sub>3</sub>/mmc" "0.8" "0" "37" "300" ""
"α" "Hexagonal" "Na<sub>3</sub>As" "P6<sub>3</sub>/mmc" "1.1" "0" "27" "300" ""
"α" "Hexagonal" "Na<sub>3</sub>As" "P6<sub>3</sub>/mmc" "1.1" "0" "30" "300" ""
"α" "Hexagonal" "Na<sub>3</sub>As" "P6<sub>3</sub>/mmc" "1.1" "0" "33" "300" ""
"α" "Hexagonal" "Na<sub>3</sub>As" "P6<sub>3</sub>/mmc" "1.1" "0" "36" "300" ""
"α" "Hexagonal" "Na<sub>3</sub>As" "P6<sub>3</sub>/mmc" "1.1" "0" "581" "300" "Photoconduction. Thin film, polycristalline"
"α" "Hexagonal" "Na<sub>3</sub>As" "P6<sub>3</sub>/mmc" "1.9" "0" "581" "300" "Optical absorption spectroscopy. Indirect transition. Single crystal, polycristalline"
"β" "Cubic" "BiF<sub>3</sub>" "Fm3m" "1.4" "0" "27" "300" ""
"β" "Cubic" "BiF<sub>3</sub>" "Fm3m" "1.4" "0" "33" "300" ""
"β" "Cubic" "BiF<sub>3</sub>" "Fm3m" "1.4" "0" "36" "300" ""
"β" "Cubic" "BiF<sub>3</sub>" "Fm3m" "1.4" "0" "581" "300" "Optical absorption spectroscopy. Single crystal"
Chart
X axis:
Y axis:
CSV Viewer: K3Sb
| Modification | CrystalSystem | StructureType | SpaceGroup | Eg | IsCalculated | ReferenceId | Temperature | Comment |
|---|---|---|---|---|---|---|---|---|
| α | Hexagonal | Na3As | P63/mmc | 1.3 | 0 | 33 | ||
| α | Hexagonal | Na3As | P63/mmc | 1.1 | 0 | 37 | 0 | |
| α | Hexagonal | Na3As | P63/mmc | 0.8 | 0 | 37 | 300 | |
| α | Hexagonal | Na3As | P63/mmc | 1.1 | 0 | 27 | 300 | |
| α | Hexagonal | Na3As | P63/mmc | 1.1 | 0 | 30 | 300 | |
| α | Hexagonal | Na3As | P63/mmc | 1.1 | 0 | 33 | 300 | |
| α | Hexagonal | Na3As | P63/mmc | 1.1 | 0 | 36 | 300 | |
| α | Hexagonal | Na3As | P63/mmc | 1.1 | 0 | 581 | 300 | Photoconduction. Thin film, polycristalline |
| α | Hexagonal | Na3As | P63/mmc | 1.9 | 0 | 581 | 300 | Optical absorption spectroscopy. Indirect transition. Single crystal, polycristalline |
| β | Cubic | BiF3 | Fm3m | 1.4 | 0 | 27 | 300 | |
| β | Cubic | BiF3 | Fm3m | 1.4 | 0 | 33 | 300 | |
| β | Cubic | BiF3 | Fm3m | 1.4 | 0 | 36 | 300 | |
| β | Cubic | BiF3 | Fm3m | 1.4 | 0 | 581 | 300 | Optical absorption spectroscopy. Single crystal |