"CrystalSystem" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "Comment" "Temperature" "StructureType" "SpaceGroup" "Glass" "1.1" "0" "27" "Thermal" "" "" "" "Glass" "1.1" "0" "36" "Thermal" "" "" "" "Glass" "0.65" "0" "27" "" "77" "" "" "Glass" "0.65" "0" "36" "" "77" "" "" "Glass" "0.72" "0" "27" "Optical" "300" "" "" "Glass" "0.72" "0" "36" "Optical" "300" "" "" "Tetragonal" "0.5" "0" "27" "" "" "Chalcopyrite" "I4(-)2d" "Tetragonal" "0.61" "0" "27" "" "" "Chalcopyrite" "I4(-)2d" "Tetragonal" "0.41" "0" "37" "" "0" "Chalcopyrite" "I4(-)2d" "Tetragonal" "0.85" "0" "27" "" "0" "Chalcopyrite" "I4(-)2d" "Tetragonal" "0.85" "0" "37" "" "0" "Chalcopyrite" "I4(-)2d" "Tetragonal" "0.56" "0" "693" "" "298" "Chalcopyrite" "I4(-)2d" "Tetragonal" "0.53" "0" "27" "" "300" "Chalcopyrite" "I4(-)2d" "Tetragonal" "0.53" "0" "37" "" "300" "Chalcopyrite" "I4(-)2d"

Chart

X axis: Y axis:

CSV Viewer: CdGeAs2

CrystalSystem Eg IsCalculated ReferenceId Comment Temperature StructureType SpaceGroup
Glass 1.1 0 27 Thermal
Glass 1.1 0 36 Thermal
Glass 0.65 0 27 77
Glass 0.65 0 36 77
Glass 0.72 0 27 Optical 300
Glass 0.72 0 36 Optical 300
Tetragonal 0.5 0 27 Chalcopyrite I4(-)2d
Tetragonal 0.61 0 27 Chalcopyrite I4(-)2d
Tetragonal 0.41 0 37 0 Chalcopyrite I4(-)2d
Tetragonal 0.85 0 27 0 Chalcopyrite I4(-)2d
Tetragonal 0.85 0 37 0 Chalcopyrite I4(-)2d
Tetragonal 0.56 0 693 298 Chalcopyrite I4(-)2d
Tetragonal 0.53 0 27 300 Chalcopyrite I4(-)2d
Tetragonal 0.53 0 37 300 Chalcopyrite I4(-)2d