"CrystalSystem" "Temperature" "E<sub>g</sub>" "IsCalculated" "ReferenceId" "Comment" "StructureType" "SpaceGroup" "Modification" "Amorphous" "300" "0.85" "0" "27" "Film" "" "" "" "Cubic" "0" "0.78" "0" "27" "Electr." "Diamond" "Fd3m" "" "Cubic" "0" "0.78" "0" "50" "Electr." "Diamond" "Fd3m" "" "Cubic" "0" "0.785" "0" "27" "Optical" "Diamond" "Fd3m" "" "Cubic" "0" "0.785" "0" "28" "Optical" "Diamond" "Fd3m" "" "Cubic" "0" "0.785" "0" "50" "Optical" "Diamond" "Fd3m" "" "Cubic" "1.5" "0.744" "0" "30" "" "Diamond" "Fd3m" "" "Cubic" "1.5" "0.744" "0" "31" "" "Diamond" "Fd3m" "" "Cubic" "1.5" "0.744" "0" "37" "" "Diamond" "Fd3m" "" "Cubic" "4.2" "0.741" "0" "31" "" "Diamond" "Fd3m" "" "Cubic" "291" "0.664" "0" "30" "" "Diamond" "Fd3m" "" "Cubic" "291" "0.664" "0" "31" "" "Diamond" "Fd3m" "" "Cubic" "291" "0.67" "0" "37" "" "Diamond" "Fd3m" "" "Cubic" "298" "0.66" "0" "72" "Indirect transition" "Diamond" "Fd3m" "" "Cubic" "298" "0.664" "0" "72" "Indirect transition" "Diamond" "Fd3m" "" "Cubic" "298" "0.67" "0" "72" "Indirect transition" "Diamond" "Fd3m" "" "Cubic" "298" "0.7" "0" "72" "Indirect transition" "Diamond" "Fd3m" "" "Cubic" "300" "0.66" "0" "27" "" "Diamond" "Fd3m" "" "Cubic" "300" "0.66" "0" "37" "" "Diamond" "Fd3m" "" "Cubic" "300" "0.67" "0" "27" "Optical" "Diamond" "Fd3m" "" "Cubic" "300" "0.67" "0" "37" "Optical" "Diamond" "Fd3m" "" "Cubic" "300" "0.7" "0" "37" "" "Diamond" "Fd3m" "" "Cubic" "300" "0.78" "0" "27" "Film" "Diamond" "Fd3m" "" "Monoclinic" "" "0.962" "1" "1540" "Quasi-direct. Calculation. CASTEP" "" "P2/m" "J"

Chart

X axis: Y axis:

CSV Viewer: Ge

CrystalSystem Temperature Eg IsCalculated ReferenceId Comment StructureType SpaceGroup Modification
Amorphous 300 0.85 0 27 Film
Cubic 0 0.78 0 27 Electr. Diamond Fd3m
Cubic 0 0.78 0 50 Electr. Diamond Fd3m
Cubic 0 0.785 0 27 Optical Diamond Fd3m
Cubic 0 0.785 0 28 Optical Diamond Fd3m
Cubic 0 0.785 0 50 Optical Diamond Fd3m
Cubic 1.5 0.744 0 30 Diamond Fd3m
Cubic 1.5 0.744 0 31 Diamond Fd3m
Cubic 1.5 0.744 0 37 Diamond Fd3m
Cubic 4.2 0.741 0 31 Diamond Fd3m
Cubic 291 0.664 0 30 Diamond Fd3m
Cubic 291 0.664 0 31 Diamond Fd3m
Cubic 291 0.67 0 37 Diamond Fd3m
Cubic 298 0.66 0 72 Indirect transition Diamond Fd3m
Cubic 298 0.664 0 72 Indirect transition Diamond Fd3m
Cubic 298 0.67 0 72 Indirect transition Diamond Fd3m
Cubic 298 0.7 0 72 Indirect transition Diamond Fd3m
Cubic 300 0.66 0 27 Diamond Fd3m
Cubic 300 0.66 0 37 Diamond Fd3m
Cubic 300 0.67 0 27 Optical Diamond Fd3m
Cubic 300 0.67 0 37 Optical Diamond Fd3m
Cubic 300 0.7 0 37 Diamond Fd3m
Cubic 300 0.78 0 27 Film Diamond Fd3m
Monoclinic 0.962 1 1540 Quasi-direct. Calculation. CASTEP P2/m J